Chemical Composition
According To EN 10027-1 & CR 10260 | C % max. | Si % max. | Mn % | P % | S % max. | N % max. | Cr % | Cu % | V% | Ni% | Z% | Mo% |
S235J2W | 0.13 | 0.4 | 0.20-0.60 | 0.04 | 0.03 | - | 0.40-0.80 | 0.25-0.55 | - | 0.65 | - | - |
S355J0W | 0.12 | 0.75 | 1 | 0.06-0.15 | 0.04 | 0.01 | 0.30-1.25 | 0.25-0.55 | - | 0.65 | - | - |
S355J2WP | 0.12 | 0.75 | 1 | 0.06-0.15 | 0.03 | - | 0.30-1.25 | 0.25-0.55 | - | 0.65 | - | - |
S355J0W | 0.16 | 0.5 | 0.50-1.50 | 0.04 | 0.04 | 0.01 | 0.40-0.80 | 0.25-0.55 | - | 0.65 | 0.15 | 0.3 |
S355J2W | 0.16 | 0.5 | 0.50-1.50 | 0.03 | 0.03 | - | 0.40-0.80 | 0.25-0.55 | - | 0.65 | 0.15 | 0.3 |
S355K2W | 0.16 | 0.5 | 0.50-1.50 | 0.03 | 0.03 | - | 0.40-0.80 | 0.25-0.55 | - | 0.65 | 0.15 | 0.3 |
According To ASTM & ASME Specn. | ||||||||||||
A 588 Gr. A | 0.19 | 0.3- 0.65 | 0.80-1.25 | 0.04 | 0.05 | - | 0.40-0.65 | 0.25-0.40 | 0.02- 0.10 | |||
A 588 Gr. B | 0.2 | 0.15- 0.50 | 0.75-1.35 | 0.04 | 0.05 | - | 0.40-0.70 | 0.20-0.40 | 0.01- 0.10 | |||
A 588 Gr. C | 0.15 | 0.15- 0.40 | 0.80-1.35 | 0.04 | 0.05 | - | 0.30-0.50 | 0.20-0.50 | 0.01- 0.10 | |||
A 588 Gr. K | 0.17 | 0.25- 0.50 | 0.50-1.20 | 0.04 | 0.05 | - | 0.40-0.70 | 0.30-0.50 | - | Cb-0.005 -0.05 | ||
A 242 Type-1 | 0.15 | - | 1 | 0.15 | 0.05 | 0.20 min. | ||||||
A 242 Type-2 | 0.20 | - | 1.50 | 0.04 | 0.05 | 0.20 min. | ||||||
According To IS STD. | ||||||||||||
IRSM-41 | 0.1 | 0.30- 0.50 | 0.25-0.45 | 0.075-0.14 | 0.03 | - | 0.35-0.49 | 0.30-0.60 | 0.05 | 0.28- 0.49 | - | 0 |